Nitrile
Examination Gloves (Online chlorinated)
|
|
Functional Benefits
|
•
|
Protection
from unwanted and dangerous substances.
|
•
|
Beaded
cuff ensures easy donning and prevent roll down.
|
•
|
Superior
strength with better puncture resistant.
|
•
|
Full
textured enhances wet and dry grip.
|
•
|
Thinner
gauge improves tactile sensitivity.
|
•
|
Custom
design enhances comfort and fit.
|
•
|
Provide
an alternative solution for individuals who are allergic
to natural rubber latex.
|
|
|
Quality Standards
|
•
|
Conforms
to ASTM D6319 (00a) and EN455 Standards.
|
•
|
Manufactured
under QSR (GMP) and ISO9001 : 2000 Quality Management
System.
|
•
|
Biocompatibility
tested or biocompatibility friendly.
|
•
|
Manufactured
from 100% nitrile (Acrylonitrile-butachiene).
|
•
|
Resists
permeation by wide range of chemicals than natural
rubber latex of the same thickness.
|
|
|
Glove sizes
|
•
|
Extra-small,
Small, Medium, Large, Extra-large.
|
•
|
Marked
in the check box on the shipping carton with black ink.
|
|
|
|
|
|
|
Product Specifications
|
Type
|
:
|
Non-sterile,
Powdered or Powder-free.
|
Material
|
:
|
Synthetic
Nitrile Latex.
|
Design
& Features
|
:
|
Ambidextrous;
fully textured; beaded cuff; natural white or coloured (blue).
|
Storage
|
:
|
The
gloves shall maintain their properties when stored in a dry
condition at temperature not higher than 30°C.
|
Moisture
Content
|
:
|
below
0.8% per glove.
|
Shelf-life
|
:
|
5
years and 3 years from date of manufacturing for Powdered and
Powder-free respectively.
|
|
|
Physical Dimensions
|
Dimensions
|
Standards
|
Top
Glove
|
ASTM
D6319 (00a)
|
Length
(mm)
|
240
min
|
220
min (size Xs, S)
230 min (size M, L, XL)
|
Width
(mm)
•
Extra-small
• Small
•
Medium
• Large
•
Extra-large
|
76 ± 3
84 ± 3
94 ± 3
105 ± 3
113 ± 3
|
70 ± 10
80 ± 10
95 ± 10
110 ± 10
120 ± 10
|
Thickness
- single wall (mm)
•
Fingers
• Palm
• Cuff
|
0.14 ± 0.03
0.11 ± 0.03
0.09 ± 0.03
|
0.05 min
0.05 min
|
|
|
Physical Properties
|
Property
|
ASTM
D6319 (00a)
|
Elongation
at break (%)
•
Before Aging
• After
Aging
|
Min 500
Min 400
|
Tensile
Strength (MPa)
•
Before Aging
• After
Aging
|
Min 14
Min 14
|
|